TE CONNECTIVITY MFT-MT2000-NO.2-0-SP

MicroFit Small diameter, high shrink ratio, heat-shrinkable tubing MicroFit tubing is micro-sized, heat- Yet, upon heating, the same tubing low-outgassing materials. MTI000 tubing may shrinkable tubing that offers a high shrink shrinks to fit tightly on a wide range of be sterilized by radiation, ethylene oxide, ratio (up to 3:1) and fits a range of diameters substrate diameters. steam, and dry heat with no significant from .007” to .045”. It is offered in a variety of change in physical properties. materials including two medical-grade MicroFit tubing is offered in three materials: formulations from our Altera line of medical- RW-175, MT1000, and MT2000. MT1000 MT2000 tubing is made from a tough, grade, heat-shrinkable tubing products. and MT2000 meet the requirements of modified polyolefin that offers flexibility, U.S. Pharmacopeia (USP) Class VI. lubricity, and good electrical insulation MicroFit tubing provides electrical insulation, performance. MT2000’s low shrink temperature mechanical protection, and strain relief in the RW-175 and MT1000 tubings utilize a tough enables the tubing to shrink faster than other smaller, more compact medical devices and semirigid fluoropolymer. They are especially materials with similar attributes, thereby commercial electronics products suitable for applications requiring high- reducing the risk of damage to temperature- manufactured today. MicroFit tubing’s temperature performance, outstanding sensitive substrates. MT2000 tubing may high shrink ratio eases installation since resistance to abrasion and cut-through, be sterilized by gamma radiation or the tubing’s diameter is large enough to slide and excellent resistance to a variety of fluids. ethylene oxide with no significant change easily over the micro-sized substrate. RW-175 meets NASA requirements for in physical properties. Temperature rating RW-175, MT1000 Full recovery temperature: 175°C Continuous operating temperature: –55°C to 175°C Recommended maximum temperature 135°C for use as a primary insulator: MT2000 Full recovery temperature: 140°C Continuous operating temperature: –40°C to 105°C Specifications* Type Raychem Material Master File Number RW-175 RW-175 MicroFit SCD MT1000, MT2000 Altera MicroFit SCD USP Class VI MAF-444 (MT1000), MAF-727 (MT2000) *When ordering, always specify latest issue. Dimensions (millimeters/inches) W1 W2 Expanded as supplied Fully recovered after heating D d Inside diameter Wall thickness D (min.) d (max.) W1 W2 (max.) Expanded Recovered after As supplied Recovered Part number as supplied heating (nominal) after heating**** MFT-**-No. 1-*** 0.356 0.014 0.178 0.007 0.076 0.003 0.127 0.005 MFT-**-No. 2-*** 0.610 0.024 0.305 0.012 0.064 0.0025 0.152 0.006 MFT-**-No. 33-*** 1.143 0.045 0.432 0.017 0.064 0.0025 0.118 0.007 MFT-**-No. 65-*** 0.635 0.025 0.254 0.010 0.127 0.005 0.330 0.013 **Replace double asterisk with material number: RW-175, MT1000 or MT2000 ***Replace triple asterisk with color-code number. ****Wall thickness will be less if tubing recovery is restricted during shrinkage. Ordering information Colors RW-175, MT1000 MT2000 Standard Clear Black, clear Nonstandard Black White, red, yellow, blue, orange Size selection Always order the largest size that will shrink snugly over the component being covered. A variety of special order sizes may be made available upon request. Standard packaging In 4-foot lengths (RW-175); on plastic spools, double-bagged (MT1000, MT2000) Ordering description Specify product name, material type, size, and color; for example, MFT-MT2000-No.1-0 (0=Black). RW-175 MicroFit specification values Property Unit Requirement Method of test PhysicalDimensions mm (inches) See reverse ASTM D 2671 Tensile strength psi (MPa) 5000 (34.5) minimum ASTM D 2671 2” per minute Ultimate elongation percent 150 minimum ASTM D 2671 2” per minute 5 Secant modulus (expanded) psi (MPa) 1 x 10 (690) minimum ASTM D 2671 Heat shock No dripping, flowing AMS-DTL-23053, (4 hours at 300°C/572°F) or cracking 5/16” mandrel Low temperature flexibility No cracking after wrapping ASTM D 2671 (4 hours at -55°C/-67°F) on mandrel Procedure C 5/16” mandrel Electrical Dielectric strength volts/mil (volts/mm) 800 (31,500) minimum ASTM D 2671 Altera MicroFit specification values Property Unit Requirement Method of test PhysicalDimensions mm (inches) See reverse ASTM D 2671 Tensile strength psi (MPa) ASTM D 2671 MT1000 5000 (34.5)minimum 2” per minute MT2000 3000 (20.7) minimum Ultimate elongation percent ASTM D 2671 MT1000 150 minimum 2” per minute MT2000 200 minimum Secant modulus (expanded) psi (MPa) ASTM D 2671 5 MT1000 1.0 X 10 (690) minimum 4 MT2000 5.0 X 10 (344) minimum Electrical Dielectric strength volts/mil (volts/mm) ASTM D 2671 MT1000 800 (31,500) minimum MT2000 1000 (39,360) minimum Dielectric withstand seconds 60 minimum ASTM D 2671 3000 V, 60 Hz Chemical Heavy metals analysis ppm 1 maximum (total of all metals) USP XXII Cadmium Physiochemical Mercury Tests - Plastics Lead (See note below) Bismuth Antimony Note: Sample preparation and extraction is per USP XXII. Metals analysis may be colorimetric as described in USP XXII or by equivalent quantitive analytical method. Altera, Raychem, and MicroFit are trademarks of Tyco Electronics Corporation. Users should independently evaluate the suitability of the product for their application. Tyco Electronics Corporation 300 Constitution Drive Faraday Road 3816 Noborito, Tama-ku Asia Pacific Headquarters Menlo Park, CA 94025-1164 Dorcan, Swindon, SN3 5HH Kawasaki, Kanagawa 214-8533 26 Ang Mo Kio, Industrial Park 2 USA United Kingdom Japan Singapore 569507 Tel:(800) 926-2425 (US & Canada) Tel: +44 1793 528171 Tel: +81 44 900 5102 Tel: +65 4866 151 Tel:+1 (650) 361-3860 (All other countries) All information, including illustrations, is believed to be reliable. Users, however, should independently evaluate the suitability of each product for their application. Tyco Electronics Corporation makes no warranties as to the accuracy or completeness of the information, and disclaims any liability regarding its use. Tyco Electronics Corporation’s only obligations are those in the Standard Terms and Conditions of Sale for these products and in no case will Tyco Electronics Corporation be liable for any incidental, indirect, or consequential damages arising from the sale, resale, use, or misuse of the product. Tyco Electronics Corporation’s Specifications are subject to change without notice. In addition, Tyco Electronics Corporation reserves the right to make changes in materials or processing without notification to the Buyer which do not affect compliance with any applicable specification. For more information about this product visit www.tycoelectronics.com © 1997, 2002 Tyco Electronics Corporation Printed in USA 1654059 6/02