TE CONNECTIVITY SAS-115-075-1017-1X

CUSTOMER DRAWING Slit Adhesive Sleeve (S-1017) Table 1: Dimensions (inches) PART DESCRIPTION EXTRUDED ID CUT LENGTH EXTRUDED WALL (A) (B) (C) SAS-090-038-1017 .090 ± .005 0.38 ± .050 0.024 ± .005 SAS-090-075-1017 .090 ± .005 0.75 ± .050 0.024 ± .005 SAS-090-1-1017 .090 ± .005 1.00 ± .050 0.024 ± .005 SAS-115-075-1017 .115 ± .005 0.75 ± .050 0.032 ± .005 SAS-115-1-1017 .115 ± .005 1.00 ± .050 0.032 ± .005 SAS-160-075-1017 .160 ± .005 0.75 ± .050 0.032 ± .005 SAS-160-1-1017 .160 ± .005 1.00 ± .050 0.032 ± .005 SAS-200-075-1017 .200 ± .005 0.75 ± .050 0.035 ± .005 SAS-200-1-1017 .200 ± .005 1.00 ± .050 0.035 ± .005 Color: Amber TITLE: Tyco Electronics Corp. Raychem 300 Constitution Drive, SPLIT ADHESIVE SLEEVE Menlo Park, CA. 94025 Molded Parts DOCUMENT NO.: Unless otherwise specified, dimensions are in inches. [Metric dimensions are shown in brackets] SAS-XXX-XXX-1017 TOLERANCES: ANGLES: Tyco Electronics reserves the right to amend this 0.00 N/A N/A drawing at any time. Users should evaluate the REVISION: DATE: 0.0 N/A suitability of the product for their application. 0 N/A ROUGHNES D August 14, 2008 S IN MICRON PREPARED BY: ECO NUMBER: CAGE CODE : SCALE: SIZE: SHEET: UNGUYEN ECO-08-020204 06090 -NA- A 1 of 3 © 2004 –2008 Tyco Electronics Corporation. All rights reserved. If this document is printed it becomes uncontrolled. Check for the latest revision. CUSTOMER DRAWING Table 2: Properties Property Unit Requirements Test Method Physical Visual -- No foreign matter, voids, pinholes. Specific Gravity -- 0.95 ± 0.05 ASTM D 792 Softening Point °C 120 ± 10 ASTM E 28 Low Temperature °C -20 maximum ASTM D 746 Impact Brittleness Adhesive Peel lbs/in width Note 1 Polyolefin 20 minimum Polychloroprene 10 minimum Polyvinylchloride 15 minimum Chemical* Water Absorption Percent 1.0 maximum ASTM D 570 Fungus Resistance -- Rating of 1 or less ASTM G 21 Fluid Resistance* Percent ASTM D 543 Weight Change after 7 days/23 ± 3°C (75 ± 5°F) 3 X 1-inch specimens Detergent Solution (#12) 3 maximum Hydraulic Fluid (MIL-PRF-87257 10 maximum or MIL-PRF-83282 ) Lube Oil (MIL-PRF-7808L) 5 maximum ASTM Oil (#49) 15 maximum Electrical* 10 Volume Resistivity ohm-cm 10 minimum ASTM D 257 Dielectric Strength V/mil 500 minimum ASTM D 149 *Test specimens shall be prepared in the form of 6 x 6 x .075-inch compression molded slabs. Molding temperature shall be 150 ± 3°C (302 ± 5°F). Acceptance Tests: Visual, Dimensions, Specific Gravity DOCUMENT NO.: ECO NUMBER: REV.: DATE: SHEET: ECO-08-020204 August 14, 2008 SAS-XXX-XXX-1017 D 2 of 3 © 2004 -2008Tyco Electronics Corporation. All rights reserved. If this document is printed it becomes uncontrolled. Check for the latest revision. CUSTOMER DRAWING Note 1: Adhesive Peel Strength Polyolefin Shrink a 6-inch length of size 1-1/2 inch tubing RNF-100 Type 2* on a glass-laminated plastic or metal tube, 1 inch in diameter, and approximately 1 foot long, with a Thermofit Model 500B Thermogun* or equivalent. Cool to room temperature, lightly abrade with No. 320 emery cloth, and + wipe with MEK. Spiral wrap S-1017 tape on the recovered tubing, with a 50% overlap. Place a strip of 3/4-inch-wide masking tape lengthwise on the adhesive tape to hold it in place and to provide unbonded ends to insert into the tensile tester. Abrade and clean the inside surface of three 1-1/2 inch lengths of size 1-1/2 inch RNF-100 Type 2. Place them on the prepared mandrel so that they are about 1/2 inch apart, and shrink with the Thermogun. Place the assembly in an oven for 10 minutes at 150 ± 3°C (302 ± 5°F). Cool to room temperature, and cut along one edge of the masking tape to remove the bonded assembly from the mandrel. Cut a 1-inch wide specimen from the center of each double thickness. Insert the unbonded ends in a tensile tester operating at 2 inches per minute. Make readings of peel strength at every 1/2 inch of jaw separation after 1 inch initial separation. The average of 5 readings shall define peel strength. Polychloroprene Repeat above procedure, except use NTFR* tubing. Polyvinylchloride Repeat above procedure, except use Thermofit PVC* tubing. *Obtainable from Tyco Electronics/Raychem Corporation. +S-1017 tape is made from the same lot of material as SAS-1017. Tyco Electronics Corporation/Raychem reserves the right to amend this specification at any time. Users should evaluate the suitability of the product for their application. DOCUMENT NO.: ECO NUMBER: REV.: DATE: SHEET: ECO-08-020204 August 14, 2008 SAS-XXX-XXX-1017 D 3 of 3 © 2004 -2008Tyco Electronics Corporation. All rights reserved. If this document is printed it becomes uncontrolled. Check for the latest revision.