TE CONNECTIVITY SAS-160-1-1030-0

INTERCONNECT ® No: SAS-XXX-X-1030 Thermofit Tubing Slit Adhesive Sleeve Specification Control Drawing Rev: C Date: February 3, 2000 Page: 1 of 3 Slit Adhesive Sleeve (S-1030) Table 1: Dimensions (inches) Size Extruded ID (A) Cut Length (B) Extruded Wall (C) SAS-090-1-1030 .090 ± .005 1.000 ± .050 0.022 ± .003 SAS-115-1-1030 .115 ± .005 1.000 ± .050 0.030 ± .003 SAS-160-1-1030 .160 ± .005 1.000 ± .050 0.030 ± .003 SAS-200-1-1030 .200 ± .005 1.000 ± .050 0.033 ± .003 SAS-250-1-1030 .250 ± .005 1.000 ± .050 0.033 ± .003 SAS-300-1-1030 .300 ± .005 1.000 ± .050 0.060 ± .003 Color: Black If this document is printed it becomes uncontrolled. Check for the latest revision. INTERCONNECT ® No: SAS-XXX-X-1030 Thermofit Tubing Slit Adhesive Sleeve Specification Control Drawing Rev: C Date: February 3, 2000 Page: 2 of 3 Table 2: Properties Property Unit Requirements Test Method Physical Visual -- No foreign matter, voids, pinholes. Specific Gravity -- 1.00 ± 0.05 ASTM D 792 Low Temperature °C -70 maximum ASTM D 746 Impact Brittleness Procedure B Adhesive Peel lbs/in width Note 1 Polyolefin 25 minimum Polychloroprene 25 minimum Chemical* Water Absorption Percent 1.0 maximum ASTM D 570 Fungus Resistance -- Rating of 1 or less ASTM G 21 Electrical* 10 Volume Resistivity ohm-cm 10 minimum ASTM D 257 Dielectric Strength V/mil 500 minimum ASTM D 149 *Test specimens shall be prepared in the form of 6 x 6 x 6 x .075-inch compression molded slabs. Molding temperature shall be 140°C (285°F). Acceptance Tests: Visual, Dimensions, Specific Gravity If this document is printed it becomes uncontrolled. Check for the latest revision. INTERCONNECT ® No: SAS-XXX-X-1030 Thermofit Tubing Slit Adhesive Sleeve Specification Control Drawing Rev: C Date: February 3, 2000 Page: 3 of 3 Note 1: Adhesive Peel Strength Polyolefin Shrink a 6-inch length of size 1-1/2 inch Thermofit RNF-100 Type 2* on a glass-laminated plastic or metal tube, 1 inch in diameter, and approximately 1 foot glass-laminated plastic or metal tube, 1 inch in diameter, and approximately 1 foot long, with a Thermofit Model 500B Thermogun* or equivalent. Cool to room temperature, + lightly abrade with No. 320 emery cloth, and wipe with MEK. Spiral wrap S-1030 tape on the recovered tubing, with a 50% overlap. Place a strip of 3/4-inch-wide masking tape lengthwise on the adhesive tape to hold it in place and to provide unbonded ends to insert into the tensile tester. Abrade and clean the inside surface of three 1-1/2 inch lengths of size 1-1/2 inch RNF-100 Type 2. Place them on the prepared mandrel so that they are about 1/2 inch apart, and shrink with the Thermogun. Place the assembly in an oven for 10 minutes at 150 ± 3°C (302 ± 5°F). Cool to room temperature, and cut along one edge of the masking tape to remove the bonded assembly from the mandrel. Cut a 1-inch wide specimen from the center of each double thickness. Insert the unbonded ends in a tensile tester operating at 2 inches per minute. Make readings of peel strength at every 1/2 inch of jaw separation after 1 inch initial separation. The average of 5 readings shall define peel strength. Polychloroprene Repeat above procedure, except use Thermofit NT-FR* tubing. *Obtainable from Raychem Corporation. +S-1030 tape is made from the same lot of material as SAS-1030. Raychem reserves the right to amend this specification at any time. Users should evaluate the suitability of the product for their application. If this document is printed it becomes uncontrolled. Check for the latest revision.